Alumina bodies containing alkali or alkaline earth metal compounds

ABSTRACT

A method of producing activated alumina bodies having alkali or alkaline earth metal compounds incorporated therein, the bodies suitable for adsorption and having increased capacity for adsorption of gases and the like. The method comprises providing a source of activated alumina powder and further providing an aqueous solution having an alkali or alkaline earth metal hydroxide and a water soluble alkali or alkaline earth metal salt of an organic compound dissolved therein. The activated alumina powder is formed into bodies which are treated with the aqueous solution to provide alumina bodies having alkali or alkaline earth metal compounds incorporated therein. The alumina bodies are heated for purposes of activation to provide said activated alumina bodies capable of having increased adsorption capacity.

BACKGROUND OF THE INVENTION

This invention relates to activated alumina and more particularly, itrelates to alumina or alumina bodies containing alkali metal compoundssuch as sodium compounds suitable for use as an adsorbent, for example.

In forming bodies of alumina suitable for adsorbing HCl, H₂ O, CO₂ or H₂S, for example, the bodies can be formed by several methods. Forexample, alumina powder can be mixed with water to make paste which isextruded to form pellets. Or, a rotating pan may be used where dryactive alumina powder is added to the pan and an aqueous solutionsprayed on the powder as the pan rotates. The rotating pan forms thepowder and solution into spheres. In another method, spheres can be madefrom a viscous slurry of the activated alumina and aqueous solutionusing the so-called "oil drop" method.

U.S. Pat. No. 4,273,735 discloses forming spheroidal alumina shapedarticles by dispersing an ungelled admixture of an alumina sol andhexamethylenetetramaine, in the form of droplets, into a liquid formingmedium which is very slightly miscible with water, the medium being at atemperature of between about 50° and 105° C.; next the alumina spheresare aged at a temperature greater than about 105° C. at superatmosphericpressure, then the alumina spheres are aged in a basic medium, beforewashing, drying and calcining. The resultant shaped articles are usefulas catalysts or catalyst carriers/supports.

U.S. Pat. No. 5,238,611 discloses a process for producing granulatedparticles from a powder which is insoluble in water. The formedgranulated particles are substantially larger than those of the powdergrains. The powder is mixed with an aqueous solution of a cellulosechosen from among methyl cellulose, hydroxypropyl methyl cellulose,etheric hydroxybutyl methyl cellulose. Then droplets of this mixture aremade to fall into an aqueous solution of at least one metallic salt ormetallic hydroxide which does not react with the particles.

U.S. Pat. No. 4,999,323 discloses production of ceramic powders byemulsion precipitation including contacting the emulsion with a gaseousreactant for the cation or cations that will react with the cation orcations to form a precipitate without breaking the emulsion. The gaseousreactant may be ammonia, which may be contacted with the emulsion untilit reaches a pH of about 10 to 11.

U.S. Pat. No. 5,032,555 discloses a process for makingzirconia-toughened alumina (ZTA) from precursor salts. The precursorsalts are coprecipitated from solution to yield a gel in a liquid phase.The gel in excess of the critical temperature and pressure is dried at atemperature and pressure in excess of the critical temperature andpressure of the liquid phase to thereby convert the liquid phase to agas. The solid particles, when separated from the gas, form a fineparticulate ZTA which, upon consolidation yields near theoreticaldensity toughened ceramics.

U.S. Pat. No. 4,166,100 discloses a method of preparing granulatedactivated alumina comprising decomposition of alumina trihydrate byheating, mixing of the obtained product of decomposition with water, itshydration, granulation, drying at a temperature of 20°-150° C., andcalcining at a temperature of 400°-600° C., in which, according to theinvention alumina trihydrate is decomposed by bringing it in contactwith a bed of a solid heat carrier having the temperature of 350°-600°C., for a period of time from 0.05 to 0.5 second, to obtain an amorphousaluminum hydroxide, which is mixed with water into a suspension havingthe concentration of 100-500 g/liter (as Al₂ O₃), with subsequenthydration of this product of decomposition at a temperature of 20°-100°C. and the pH of 5-12 for 0.5-10 hours; before granulation of thehydrated product of decomposition, it is treated with an acid, that canform water-soluble basic salts of aluminum, at a temperature of 20°-150°C.

U.S. Pat. No. 5,316,998 discloses an HCl adsorbent, and method of makingand using the adsorbent, the adsorbent comprising an activated aluminapromoted with an alkali metal oxide. The adsorbent contains at leastabout 5% alkali metal oxide. This patent discloses adding the alkalimetal oxide using an alkali metal salt of an organic compound thatdecomposes at temperatures below 500° C. and liberates the organicportion.

U.S. Pat. No. 3,222,129 discloses partially dehydrated material groundso that the particles are extremely small, e.g., on the order of one totwo microns. The ground particles are mixed with water to formagglomerated nodules and heated to low temperatures, e.g., about 100°C., for a period of several hours to cure the nodules. The curedmaterial is activated by heating to a temperature in excess of 700° F.for a period of time.

U.S. Pat. No. 5,288,849 discloses alumina-based adsorbents containing atleast one compound of an alkali or alkaline earth metal, wherein thealkali or alkaline earth metal values are present in an amount rangingfrom 15 mmole to 100 mmole per 100 g of alumina, are useful for theadsorptive purification of polyolefins prepared by the polymerization ofolefins in the presence of a metallic coordination catalyst, to removecontaminating catalyst metal values therefrom with but negligiblemonomer/solvent isomerization.

British Patent 2,267,096 discloses a solid particulate absorbentmaterial for removing acidic contaminants from hydrocarbons comprisingsodium hydroxide and/or potassium hydroxide, alumina and/or zinc oxide,lime, and optionally, copper II oxide. A hydrocarbon containing anacidic contaminant is purified by passing the hydrocarbon through a bedof the particulate absorbent material.

U.S. Reissue Patent 30,569 discloses that hard, rounded aggregates areproduced by preparing droplets of a slurry consisting of suspendingliquid containing distinct particles of a solid and dropping thedroplets of the slurry onto a bed of particles under conditions wherethe suspending liquid of the slurry droplet is removed. This techniqueis especially desirable for making unique fixed-bed catalysts.

Canadian Patent 811,641 discloses forming refractory spheres by drippinga resinous mixture into an alkaline solution. Other powder-relatedpatents include U.S. Pat. Nos. 5,266,243; 5,340,781; 4,952,144;3,495,954 and Japanese Patent 54011-076. However, there is still a greatneed for improved alumina bodies having increased alkali or alkalineearth metal compounds incorporated therein and an improved process forproviding the same.

SUMMARY OF THE INVENTION

It is an object of the invention to provide an improved process forforming alumina bodies incorporating sodium containing compounds.

It is another object of this invention to provide an improved processfor incorporating alkali or alkaline earth metals or compounds such asNa-containing compounds into alumina bodies.

Yet it is a further object of this invention to provide a process fortreating activated alumina powder with an aqueous solution containingalkali or alkaline earth metal hydroxide such as sodium hydroxide.

Still, it is another object of the invention to provide a process forincorporating high levels of Na or Na compounds, for example, intoactivated alumina powder as it is formed into bodies or nodules bytreating the bodies with a spray of an aqueous solution containingalkali or alkaline earth metal hydroxides, e.g., NaOH, at a pH greaterthan 11.

These and other objects will become apparent from a reading of thespecification and claims appended hereto.

In accordance with these objects, there is provided a method ofproducing activated alumina bodies having alkali or alkaline earth metalcompounds incorporated therein, the bodies suitable for adsorption andhaving increased capacity for adsorption of gases and the like. Themethod comprises providing a source of activated alumina powder andfurther providing an aqueous solution having an alkali or alkaline earthmetal hydroxide and a water soluble alkali or alkaline earth metal saltof an organic compound dissolved therein. The activated alumina powderis formed into bodies which are treated with the aqueous solution toprovide alumina bodies having alkali or alkaline earth metal compoundsincorporated therein. The alumina bodies are heated for purposes ofactivation to provide said activated alumina bodies capable of havingincreased adsorption capacity.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1 and 2 show differential thermogravimetric analysis (DTG) curvesshowing the amount of bayerite formed before and after curing.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

In accordance with the invention, there is provided a method forproducing alumina bodies having alkali or alkaline earth metal compoundsor their oxides, e.g., sodium or sodium compounds such as sodiumaluminate incorporated in the bodies. The method comprises using asource of activated alumina powder and an aqueous solution having a pHof about 12 to 14, the solution having metal hydroxide, e.g., NaOH orKOH, dissolved therein. The activated alumina powder is formed intoalumina bodies, e.g., rounded bodies, using the high pH aqueous solutionto bond particles of the alumina powder together by rehydration. Usingthe high pH solution results in efficiently incorporating substantiallevels of the alkali or alkaline earth metals or their oxides into thealumina body to provide for improved properties such as increasedsurface area and crush strength.

The activated alumina referred to includes alumina having a surface areausually greater than 100 m² /g and typically in the range of 100 to 400m² /g. Further, the activated alumina powder is preferably obtained byrapid dehydration of aluminum hydroxides, e.g., alumina trihydrate orhydrargillite in a stream of hot gasses or solid heat carrier.Dehydration may be accomplished in any suitable apparatus using thestream of hot gases or solid heat carrier. Generally, the time forheating or contacting with the hot gases is a very short period of time,typically from a fraction of a second to 4 or 5 seconds, for example.Normally, the temperature of the gases varies between 400° and 1000° C.The process is commonly referred to as flash calcination and isdisclosed in U.S. Pat. No. 2,915,365, incorporated herein by reference.However, other methods of calcination may be employed.

The activated alumina suitable for use in the present invention forforming agglomerates has a median particle size in the range of 0.1 to300 microns, preferably 1 to 100 microns and typically 1 to 20 microns.In certain instances, it may be desirable to use a median particle sizeof 1 to 10 microns. The activated alumina typically has an LOI (loss ofignition) in the range of about 5 to 12% at a temperature of 200° to1000° C. The alumina may be ground to the desired particle size beforeor after activation.

One source of activated alumina is gibbsite which is one form of aluminahydrate derived from bauxite using the Bayer process. However, alphaalumina monohydrate, pseudoboehmite or the alumina trihydrate may beused if sufficiently calcined. Other sources of alumina may also beutilized including clays and aluminum alkoxides.

For purposes of the present invention, the aqueous solution is providedat a pH of at least 12, preferably a pH of at least 12.5 and furtherpreferably the pH should be in the range of about 12.5 to 14. Typically,the pH of the aqueous solution is provided in the range of about 12.7 toabout 13.8. For purposes of providing sodium containing alumina, the pHof the aqueous solution may be obtained by the addition of sodiumhydroxide. That is, sufficient sodium hydroxide is added to the aqueoussolution to provide the desired pH. If it is desired to providepotassium containing alumina, the pH of the solution may be obtained bythe addition of potassium hydroxide. Also, for purposes of providingalumina bodies containing more than one metal or metal oxide, such assodium and potassium, the pH of the solution can be adjusted by addingboth metal hydroxides, for example, sodium hydroxide and potassiumhydroxide, and such is contemplated within the perview of the invention.

Also, for purposes of increasing the rate of reaction, the temperatureof the aqueous solution can be applied to the alumina bodies or duringthe forming of the alumina bodies at a temperature from room temperatureto about 200° F., typically 100° to 190° F., with a preferredtemperature range being 120° to 160° F.

For purposes of incorporating or modifying the activated alumina withalkali, alkaline earth metal or a compound containing the alkali oralkaline earth metal, e.g., sodium or sodium-containing compoundcontained in an aqueous solution, the activated alumina is treated withthe aqueous solution in the pH range set forth above. For example, theactivated alumina can be mixed with the aqueous solution to provide aviscous slurry. The slurry can be extruded thereby providing pellets oragglomerates of the activated alumina and the sodium in the solution.Alternatively, the slurry can be formed into spheres by the oil dropmethod.

In another method, the aqueous solution is brought in contact with theactivated alumina during the step of forming the activated alumina intorounded bodies such as spheres, for example. This method of formingrounded bodies or agglomerates involves the use of a rotating pan or pannodulizer wherein activated alumina powder is fed to the pan at a steadyrate. Concurrently with feeding the alumina to the pan, the aqueoussolution is sprayed on the activated alumina bodies or agglomerates asthey are formed. Thus, activated alumina powder is steadily turned intobodies or agglomerates having alkali or alkaline earth metal compoundscombined therewith.

While the preferred method of forming activated alumina bodiescontaining, for example, Na or Na-containing compounds is the use of apan nodulizer, it should be understood that any method of incorporatinga sodium promotor into the bodies of alumina may be used. For example,bodies comprised of activated alumina may be treated with the high pHsolution.

The use of a high pH aqueous solution in accordance with the inventionhas the effect of delivering substantial levels of alkali or alkalineearth metal such as sodium or sodium-containing compound to the aluminasurface to permit reaction with the alumina. While the inventor does notwish to be bound by any theory of invention, it is believed that thehigh pH as well as delivering Na to the activated alumina surface hasthe effect of promoting a reaction between alumina and the alkali metal,e.g., sodium. The high pH is believed to have a combination of effects.That is, the alumina is dissolved layer by layer in the alkalinesolution and then the more insoluble and stable bayerite isre-precipitated on the remaining surface area. At higher pH, thedissolution and re-precipitation reaction is accelerated. As a result,less original calcined alumina grains remain and more cementation bondsof bayerite or pseudo-boehmite are formed between residual calcinedalumina grains. In addition, it is believed that the reaction betweenalkali metal hydroxide, e.g., sodium hydroxide, and alumina leads to analuminate surface species, e.g., sodium aluminate, upon heating toactivation. The formation of soluble sodium aluminate is alsoaccelerated by a high pH. The higher levels of bayerite formation can bemeasured by thermal gravimetric analysis or x-ray diffraction analysis.

A higher level of bayerite results in a higher BET surface area inalumina nodules or alumina bodies formed by the process of thisinvention. Also, a higher level of bayerite in the as-formed or freshalumina bodies stimulates formation of additional bayerite upon curing.Upon activation, the bayerite decomposes to an eta-alumina phase whichis a higher surface area material.

In the present invention, increased bayerite results in increased crushstrength of the nodules. This results from the increased cementatiousbonding provided by the bayerite material.

Nodules made by the process of the invention can have an increased levelof inertness. The higher levels of sodium, for example, in a form ofsurface aluminate, provides for more effective neutralization of aluminaacid sites. That is, it is believed that the strongest acid sites areinvolved in aluminate formation. Thus, the more effective neutralizationof the acid sites on the alumina leads to a higher level of inertness inthe activated alumina nodules or bodies.

In the present invention, it has been discovered that the sodium,calculated as sodium oxide (Na₂ O) can be increased substantially as thepH is increased in accordance with the invention. Thus, the Na₂ Ocontent can be increased from about 0.3 wt. % at a pH of 12 to about 1.3wt. % at a pH of 13 when formed, for example, by pan nodulizing.

After formation, the alumina bodies are cured or dried for purposes ofrehydration which can occur from room temperature to temperatures up toabout 200° C. Further, the time for curing can range from a few minutesup to 25 hours or more, depending on the conditions. During curing,water may be added for purposes of rehydration. Normally, when thealumina bodies are formed from a viscous slurry or by spraying as notedabove, sufficient water is present for purposes of rehydration toprovide cured bodies. In some instances, it may not be necessary to dryor cure the bodies prior to activation. It should be noted that high pHliquid or aqueous solution present in the alumina bodies causes fastercuring and consequently a higher bayerite phase when compared to thelevel of bayerite in alumina bodies formed using a lower pH solution.

After curing, the bodies are heated for purposes of activating andremoving water of hydration. Typically, the bodies are heated to providebodies with an LOI in the range of about 2 to 6%. Normally, the bodiesare heated at a temperature in the range of about 275° to about 600° C.for removing water of hydration to the desired level. Time attemperature can range from 5 to 70 minutes. The ranges given herein areinclusive of all the numbers within the range as if specifically setforth.

When sodium hydroxide solutions are used in accordance with theinvention, activated alumina bodies formed have a surface area in therange of 300 to 450 m² /g at sodium (sodium oxide) levels of 0.3 to 7wt. %, e.g., 0.3 to 1.3 wt. %. Further, the bodies have a macro-porevolume distribution of at least 0.05 cc/g at a pore diameter of 750Angstroms and a total pore volume of at least 0.2 cc/g.

While the invention has been described particularly with respect to theuse of a sodium hydroxide or other water soluble or alkaline earthcompounds contained in aqueous solution, it should be understood thatthe invention can include other materials. For example, when it isdesired to increase the alkali metal content beyond, for example 1.2 or1.3 wt. % Na (as Na₂ O), even beyond 1.6 wt. % Na₂ O, soluble metalsalts of organic compounds can be used. That is, water soluble, alkalior alkaline earth metal salt of an organic compound can be incorporatedin the aqueous solution. Highly suitable organic salts can include Na, Kand Li organic salts. Typically, such salts include carboxylic acidsalts, including mono-, di- and tri-carboylic acids. The organic part ofthe organic salt must be capable of decomposing upon heating, forexample, during curing or activating. Normally, the carboxylic acid willnot include more than 5 carbon atoms. Such salts can include Na, K andLi salts of formates, acetates, proprinates or butyrates. Na formnate,acetate or proprionate is the organic salt that is highly suitable forincorporating at the high pH range. Na acetate is particularly suitable.

When a combination solution of alkali or alkaline earth metal hydroxideand alkali or alkaline earth metal salt of an organic compound is used,the concentration of each may be varied depending on the amount of metalcompound, e.g., Na₂ O, desired in the alumina bodies. For example, theamount of sodium acetate and sodium hydroxide may be added to water toprovide the desired concentration and pH. A substantial neutral solutioncan be used or a solution having a high pH may be used. Or, for example,a solution of sodium hydroxide can be neutralized with glacial aceticacid and then diluted to the desired concentration of sodium acetate andsodium can be added as necessary.

While the invention has been described with respect to relatively pureactivated alumina or activated alumina derived from the Bayer process,activated aluminas having substantial levels of alkali metals or alkalimetal compounds, e.g., alkali metal oxides such as Na₂ O incorporatedtherein may be used as the starting material for applying the high pHaqueous solution thereto, as noted above.

Further, activated alumina nodules or bodies containing 0.1 to 1.3 wt. %Na₂ O can be treated with a high pH solution in accordance with theinvention. When the high pH solution utilizes a sodium hydroxidesolution, the level of Na₂ O can be increased from about 0.1 to 1 wt. %above the initial sodium level. Thus, it will be seen that the level ofNa₂ O, for example, can be increased substantially in existing nodulesor bodies by applying the sodium hydroxide solution in the pH range inaccordance with the invention. Further, the level of alkali or alkalineearth metal, e.g., Na₂ O, can be increased substantially, if thesolution contains alkali or alkaline earth metal salt of an organiccompound, and such is contemplated within the invention. The hydroxidesolution with or without the alkali or alkaline earth metal salt of anorganic compound can be applied by spraying as the nodules or bodies arecirculated in a rotating pan nodulizer or the nodules or bodies can bedipped in the solution. Thereafter, the bodies are heated for purposesof activation. Similarly, the solution can be applied by spraying seedbodies of alumina on a rotating pan nodulizer simultaneously withaddition of alumina powder to provide nodules or bodies having increasedlevels of Na₂ O.

Alumina bodies produced in accordance with the present invention areuseful as a drying agent, an adsorbent, a catalyst or catalyst support,for example. When used as an adsorbent, the bodies are very effective inremoving HCl, oxides of nitrogen, organic acids, H₂ S and othercontaminants from industrial waste streams. Because the alumina bodiesof the invention have high surface area and crush strength, they areparticularly effective as an adsorbent for either gas or liquid streams.

The following examples are further illustrative of the invention.

EXAMPLE 1

In this example, Gibbsite powder was flash calcined and then fed to apan nodulizer. It was sprayed with various aqueous sodium hydroxidesolutions (pH=8.3, 12.8, 13.0 and 13.2) while forming nodules. Theaverage size of the nodules was about 3 mm in diameter. The nodules werecured at ambient temperature and then held for about 3 hours in a curingbin. The nodules were activated at 750° F. for about 1 hour. The resultsare provided in Table 1.

                  TABLE 1                                                         ______________________________________                                                    BET Surface                                                                            Crushing                                                             Area     Strength†                                                                         Na.sub.2 O                                    Sample   pH       m.sup.2 /gm                                                                              lb/mm length                                                                           wt. %                                   ______________________________________                                        A        8.3‡                                                                        324        28       0.3                                              NO NaOH                                                                       Addition                                                             B        12.8     328        28       0.34                                    C        13.0     337        32       0.39                                    D        13.2     352        34       0.53                                    ______________________________________                                         †average of 5 separate runs                                            ‡5 × 8 mesh nodules                                     

It will be seen that the higher pH resulted in increased surface area,crush strength and Na₂ O levels.

Nodules from the pan nodulizer (prior to curing) were subjected to X-rayanalysis and thermogravimetric analysis (TG-DTG). FIG. 1 shows thatsample D contains a substantial amount of bayerite denoted by the DTGpeak at 270° C. Sample A nodulized without a sodium hydroxide additionshowed that bayerite was not formed. FIG. 2 shows the amount of bayeriteformed after curing. It will be noted that sample D resulted insignificantly more bayerite.

EXAMPLE 2

In this example, alumina bodies were formed as in Example 1, exceptmixtures of sodium hydroxide and sodium acetate (Samples E and F) wereused for spraying the alumina bodies as they were formed. The sodiumhydroxide and sodium acetate solution was made by neutralizing a 50%sodium hydroxide solution with glacial acetic acid. This was followed bydiluting the neutralized solution with water to a 6.2 wt. % sodiumacetate. Then, sodium hydroxide was added to this solution to obtain aconcentration of 16 grams sodium hydroxide per liter of solution. Thesolution mixture in Example F provided an excess of sodium hydroxidewhich would have provided a pH of 13.3 if added to pure water. Thesamples were cured for 12 hours in a curing bin at a temperature rangeof 30 to 60° C.

                  TABLE 2                                                         ______________________________________                                                          Crushing                                                                      Strength Na.sub.2 O                                         Sample    pH     BET        lb/mm length†                                                                   wt. %                                    ______________________________________                                        E         7.2    325        14       1.25                                     F         13.3‡                                                                     355        19       1.55                                     ______________________________________                                         †measured on 8 mesh balls                                              ‡calculated from the excess sodium hydroxide                  

It will be seen that the level of Na measured as Na₂ O increasedsubstantially while maintaining high surface areas.

EXAMPLE 3

In this example, activated alumina bodies (between 7 mesh and 12 mesh(U.S. Sieve series) comprised of sodium doped alumina (1.45 wt. % Na₂ O)were rotated in a pan nodulizer while spraying with a solution of sodiumacetate and sodium hydroxide, Sample G in Table 3. The solutioncontained 380 gm Na acetate/l and 4 gm NaOH/l to provide a pH of about12.9. The alumina bodies were maintained at a temperature of about 180°F. while the solution was applied. The bodies, Sample H, were activatedat 840° F. The results are shown in Table 3. It can be seen that thealumina bodies of Sample H have increased the adsorption capacity forcarbon dioxide by 2.5 times compared to the same alumina bodies nottreated.

                  TABLE 3                                                         ______________________________________                                                     Total Pore      Carbon Dioxide                                                Volume BET      Adsorbed                                         Sample   Na.sub.2 O wt. %                                                                        cc/g     m2/gm  wt. %                                      ______________________________________                                        G        1.45      0.29     356    1.4                                        H        7.3       0.34     268    3.5                                        ______________________________________                                    

While the invention has been described in terms of preferredembodiments, the claims appended hereto are intended to encompass otherembodiments which fall within the spirit of the invention.

What is claimed is:
 1. A method of producing activated alumina bodieshaving alkali or alkaline earth metal compounds incorporated therein,the bodies suitable for adsorption and having increased capacity, themethod comprising:(a) providing a source of activated alumina powder;(b) providing an aqueous solution having an alkali or alkaline earthmetal hydroxide and a water soluble alkali or alkaline earth metal saltof an organic compound dissolved therein, the solution having a pH inthe range of 6 to 13.5; (c) forming said activated alumina powder intobodies; (d) treating said bodies with said aqueous solution to providealumina bodies having said alkali or alkaline earth metal compoundsincorporated therein; and (e) heating said alumina bodies for purposesof activation to provide said activated alumina bodies capable of havingincreased adsorption capacity.
 2. The method in accordance with claim 1wherein said organic compound is an alkali or alkaline earth metal saltof a carboxylic acid.
 3. The method in accordance with claim 1 whereinthe alkali or alkaline earth metal hydroxide is selected from the groupconsisting of sodium, potassium, calcium and lithium hydroxide.
 4. Themethod in accordance with claim 1 wherein the alkali or alkaline earthmetal salt of an organic compound is selected from the group consistingof sodium, potassium and lithium salts of formates, acetates andpropionates.
 5. The method in accordance with claim 1 wherein the alkalior alkaline earth metal hydroxide is sodium hydroxide and said alkali oralkaline earth metal salt is sodium or potassium acetate.
 6. The methodin accordance with claim 1 wherein said treating with said aqueoussolution is performed in a temperature range of from room temperature to200° F.
 7. The method in accordance with claim 1 including applying saidaqueous solution in a temperature range of 100° to 200° F.
 8. The methodin accordance with claim 1 including applying said aqueous solution in atemperature range of 120° to 180° F.
 9. The method in accordance withclaim 1 including treating said bodies as they are being formed withsaid aqueous solution.
 10. The method in accordance with claim 1including the step of forming said bodies in a rotating pan.
 11. Themethod in accordance with claim 1 wherein said treating is spraying saidaqueous solution on said bodies as they are formed.
 12. The method inaccordance with claim 1 wherein said activated alumina bodies contain0.3 to 7 wt. % Na₂ O based on the weight of alumina.
 13. The method inaccordance with claim 1 including the step of spraying formed aluminabodies with said aqueous solution.
 14. The method in accordance withclaim 1 including maintaining said formed bodies at a temperature in therange of 120° to 200° F.
 15. A method of producing activated aluminabodies, the bodies having increased adsorption capacity, the methodcomprising:(a) providing a source of activated alumina powder; (b)providing an aqueous solution comprised of sodium hydroxide and a watersoluble alkali or alkaline earth metal salt of an organic compoundselected from one of the group consisting of sodium, potassium andlithium acetate dissolved therein, the solution having a pH in the rangeof 6 to 13.5; (c) forming said activated alumina powder into bodies; (d)as said bodies are forming, spraying said bodies with said aqueoussolution to form alumina bodies having said hydroxide and acetateincorporated therein; and (e) heating said alumina bodies for purposesof activation to provide said activated alumina bodies having increasedlevels of adsorption.
 16. The method in accordance with claim 15 whereinsaid treating with said aqueous solution is performed in a temperaturerange of from room temperature to 200° F.
 17. The method in accordancewith claim 15 including applying said aqueous solution in a temperaturerange of 100° to 200° F.
 18. The method in accordance with claim 15including applying said aqueous solution in a temperature range of 120°to 180° F.
 19. The method in accordance with claim 15 wherein theorganic compound is sodium acetate.
 20. A method of producing activatedalumina bodies having alkali or alkaline earth metal compoundsincorporated therein, the bodies having increased adsorptive capacity,the method comprising:(a) providing a source of activated aluminapowder; (b) providing an aqueous solution having an alkali or alkalineearth metal hydroxide and a water soluble alkali or alkaline earth metalsalt of an organic compound dissolved therein, the solution having a pHin the range of 6 to 13.5; (c) mixing said powder and said solution toform a mixture and forming said mixture into bodies; and (d) heatingsaid alumina bodies for purposes of activation to provide said activatedalumina bodies capable of having increased adsorption capacity.
 21. Themethod in accordance with claim 20 wherein the alkali or alkaline earthmetal hydroxide is sodium hydroxide.
 22. The method in accordance withclaim 20 wherein the alkali or alkaline earth metal salt of an organiccompound is selected from the group consisting of sodium, potassium andlithium salts of formates, acetates and propionates.
 23. The method inaccordance with claim 20 wherein the alkali or alkaline earth metalhydroxide is sodium hydroxide and said organic compound is sodiumacetate.
 24. A method of producing activated alumina bodies havingalkali or alkaline earth metal compounds incorporated therein, thebodies having increased adsorption capacity, the method comprising:(a)providing formed alumina bodies; (b) providing an aqueous solutionhaving an alkali or alkaline earth metal hydroxide and a water solublealkali or alkaline earth metal salt of an organic compound dissolvedtherein, the solution having a pH in the range of 6 to 13.5; (c)treating said formed alumina bodies with said aqueous solution toprovide alumina bodies having of said alkali or alkaline earth metalcompounds incorporated therein; and (d) heating said alumina bodieshaving said metal compounds incorporated therein for purposes ofproviding activated alumina bodies capable of having increasedadsorption capacity.
 25. The method in accordance with claim 24 whereinthe alkali or alkaline earth metal salt of an organic compound isselected from the group consisting of sodium, potassium and lithiumsalts of formates, acetates and propionates.
 26. The method inaccordance with claim 24 wherein said formed alumina bodies contain 0.3to 1.6 wt. % Na₂ O based on the weight of alumina.
 27. The method inaccordance with claim 24 wherein the alkali or alkaline earth metalhydroxide is sodium hydroxide and said alkali or alkaline earth metalsalt is sodium or potassium acetate.
 28. The method in accordance withclaim 24 wherein said treating with said aqueous solution is performedin a temperature range of from room temperature to 200° F.
 29. Themethod in accordance with claim 24 including applying said aqueoussolution in a temperature range of 100° to 200° F.
 30. The method inaccordance with claim 24 including applying said aqueous solution in atemperature range of 120° to 180° F.
 31. A method of producing activatedalumina bodies having alkali or alkaline earth metal compoundsincorporated therein, the method comprising:(a) providing formed aluminabodies containing 0.3 to 1.6 wt. % Na₂ O based on the weight of alumina;(b) providing an aqueous solution having an alkali or alkaline earthmetal hydroxide selected from the group consisting of sodium andpotassium hydroxide and a water soluble alkali or alkaline earth metalsalt of an organic compound selected from the group consisting of sodiumand potassium formate, acetate or proprionate dissolved therein, thesolution having a pH in the range of 6 to 13.5; (c) maintaining saidbodies in a temperature range of 120° to 200° F.; (d) treating saidbodies with said aqueous solution to provide alumina bodies having saidalkali or alkaline earth metal compounds incorporated therein; and (e)heating said alumina bodies having said metal compounds incorporatedtherein for purposes of activation to provide said activated aluminabodies capable of having increased adsorption capacity.
 32. The methodin accordance with claim 31 wherein said metal hydroxide is sodiumhydroxide and the alkali or alkaline earth metal salt of an organiccompound is sodium acetate.